Are you looking for read ebook online? Search for your book and save it on your Kindle device, PC, phones or tablets. Download Stabilization of Lead-rich Low-level Mixed Wastes in Chemically Bonded Phosphate Ceramic PDF full book. Access full book title Stabilization of Lead-rich Low-level Mixed Wastes in Chemically Bonded Phosphate Ceramic by . Download full books in PDF and EPUB format.
Author: Publisher: ISBN: Category : Languages : en Pages : 12
Book Description
A chemically bonded magnesium potassium phosphate ceramic has been developed by an acid-base reaction at room temperature, for use in stabilizing U.S. Department of Energy low-level mixed waste streams that include hazardous metals and low-level radioactive elements. Using this ceramic, we solidified, in monolithic waste forms, low-level mixed waste streams containing various levels of PbCl2 and PbCO3. These final waste forms were evaluated for their land disposal suitability. The results showed low open porosity (1.48-4.61 vol.%); hence, low permeability, and higher compression strengths (4310-6734 psi) that were one order of magnitude above that required. The level of lead in the leachate following the Toxicity Characteristic Leaching Procedure test was reduced from 50,000 to
Author: Publisher: ISBN: Category : Languages : en Pages : 12
Book Description
A chemically bonded magnesium potassium phosphate ceramic has been developed by an acid-base reaction at room temperature, for use in stabilizing U.S. Department of Energy low-level mixed waste streams that include hazardous metals and low-level radioactive elements. Using this ceramic, we solidified, in monolithic waste forms, low-level mixed waste streams containing various levels of PbCl2 and PbCO3. These final waste forms were evaluated for their land disposal suitability. The results showed low open porosity (1.48-4.61 vol.%); hence, low permeability, and higher compression strengths (4310-6734 psi) that were one order of magnitude above that required. The level of lead in the leachate following the Toxicity Characteristic Leaching Procedure test was reduced from 50,000 to
Author: Publisher: ISBN: Category : Languages : en Pages : 7
Book Description
Mixed waste streams, which contain both chemical and radioactive wastes, are one of the important categories of DOE waste streams needing stabilization for final disposal. Recent studies have shown that chemically bonded phosphate ceramics may have the potential for stabilizing these waste streams, particularly those containing volatiles and pyrophorics. Such waste streams cannot be stabilized by conventional thermal treatment methods such as vitrification. Phosphate ceramics may be fabricated at room temperature into durable, hard and dense materials. For this reason room-temperature-setting phosphate ceramic waste forms are being developed to stabilize these to ''problem waste streams.''
Author: Publisher: ISBN: Category : Languages : en Pages : 10
Book Description
In an effort to develop chemically bonded phosphate ceramics for mixed waste stabilization, a collaborative project to develop iron-phosphate based ceramics has been initiated between Argonne National Laboratory and the V.G. Khlopin Radium Institute in St. Petersburg, Russia. The starter powders are oxides of iron that are generated as inexpensive byproduct materials in the iron and steel industry. They contain iron oxides as a mixture of magnetite (Fe3O4) and haematite (Fe2O3). In this initial phase of this project, both of these compounds were investigated independently. Each was reacted with phosphoric acid solution to form iron phosphate ceramics. In the case of magnetite, the reaction was rapid. Adding ash as the waste component containing hazardous contaminants resulted in a dense and hard ceramic rich in glassy phase. On the other hand, the reaction of phosphoric acid solution with a mixture of haematite and ash waste contaminated with cesium and americium was too slow. Samples had to be molded under pressure. They were cured for 2-3 weeks and then hardened by heating at 350°C for 3 h. The resulting ceramics in both cases were subjected to physical tests for measurement of density, open porosity, compression strength, phase analyses using X-ray diffraction and differential thermal analysis, and leaching tests using toxicity characteristic leaching procedure (TCLP) and ANS 16.1 with 7 days of leaching. Using the preliminary information obtained from these tests, we evaluated these materials for stabilization of Department of Energy's mixed waste streams.
Author: Publisher: ISBN: Category : Languages : en Pages : 12
Book Description
Over the last few years, Argonne National Laboratory has been developing room-temperature-setting chemically bonded phosphate ceramics for solidifying and stabilizing low-level mixed wastes. This technology is crucial for stabilizing waste streams that contain volatile species and off-gas secondary waste streams generated by high-temperature treatment of such wastes. We have developed a magnesium phosphate ceramic to treat mixed wastes such as ash, salts, and cement sludges. Waste forms of surrogate waste streams were fabricated by acid-base reactions between the mixtures of magnesium oxide powders and the wastes, and phosphoric acid or acid phosphate solutions. Dense and hard ceramic waste forms are produced in this process. The principal advantage of this technology is that the contaminants are immobilized by both chemical stabilization and subsequent microencapsulation of the reaction products. This paper reports the results of durability studies conducted on waste forms made with ash waste streams spiked with hazardous and radioactive surrogates. Standard leaching tests such as ANS 16.1 and TCLP were conducted on the final waste forms. Fates of the contaminants in the final waste forms were established by electron microscopy. In addition, stability of the waste forms in aqueous environments was evaluated with long-term water-immersion tests.
Author: Publisher: ISBN: Category : Languages : en Pages : 20
Book Description
Results of an initial investigation of low temperature setting chemically bonded magnesium ammonium phosphate (MAP) ceramics as waste form materials, for solidification and stabilization of radioactive and mixed waste, are reported. The suitability of MAP for solidifying and encapsulating waste materials was tested by encapsulating zeolites at loadings up to (approximately)50 wt%. The resulting composites exhibited very good compressive strength characteristics. Microstructure studies show that zeolite grains remain unreacted in the matrix. Potential uses for solidifying and stab wastes are discussed.
Author: Ian W. Donald Publisher: John Wiley & Sons ISBN: 1444319361 Category : Science Languages : en Pages : 526
Book Description
The safe storage in glass-based materials of both radioactiveand non-radioactive hazardous wastes is covered in a single book,making it unique Provides a comprehensive and timely reference source at thiscritical time in waste management, including an extensive andup-to-date bibliography in all areas outlined to waste conversionand related technologies, both radioactive and non-radioactive Brings together all aspects of waste vitrification, drawscomparisons between the different types of wastes and treatments,and outlines where lessons learnt in the radioactive waste fieldcan be of benefit in the treatment of non-radioactive wastes
Author: 
Author: 
Author: 
Author: 
Author: Seung-Young Jeong
Author: 
Author: 
Author: 
Author: 
Author: 
Author: Ian W. Donald