Stress corrosion cracking (SCC) in unirradiated recrystallized Zircaloy-4 internally pressurized tubing specimens in atmospheres containing iodine vapor, cesium, or combinations of iodine and cesium is evaluated experimentally in terms of the effects of internal surface flaw morphology, iodine and cesium concentrations, tubing hydrogen content, test temperature, and test atmosphere water vapor content on the time to failure. The iodine vapor SCC data are analyzed in the framework of a fracture mechanics model. Expressions are developed which relate the iodine SCC threshold stress and lifetime for stresses above threshold to temperature, iodine concentration, and surface flaw geometry.
Susceptibility of Unirradiated Recrystallized Zircaloy-4 Tubing to Stress Corrosion Cracking (LWBR Development Program).
Author:
Publisher:
ISBN:
Category :
Languages : en
Pages :
Book Description
Stress corrosion cracking (SCC) in unirradiated recrystallized Zircaloy-4 internally pressurized tubing specimens in atmospheres containing iodine vapor, cesium, or combinations of iodine and cesium is evaluated experimentally in terms of the effects of internal surface flaw morphology, iodine and cesium concentrations, tubing hydrogen content, test temperature, and test atmosphere water vapor content on the time to failure. The iodine vapor SCC data are analyzed in the framework of a fracture mechanics model. Expressions are developed which relate the iodine SCC threshold stress and lifetime for stresses above threshold to temperature, iodine concentration, and surface flaw geometry.
Publisher:
ISBN:
Category :
Languages : en
Pages :
Book Description
Stress corrosion cracking (SCC) in unirradiated recrystallized Zircaloy-4 internally pressurized tubing specimens in atmospheres containing iodine vapor, cesium, or combinations of iodine and cesium is evaluated experimentally in terms of the effects of internal surface flaw morphology, iodine and cesium concentrations, tubing hydrogen content, test temperature, and test atmosphere water vapor content on the time to failure. The iodine vapor SCC data are analyzed in the framework of a fracture mechanics model. Expressions are developed which relate the iodine SCC threshold stress and lifetime for stresses above threshold to temperature, iodine concentration, and surface flaw geometry.
Energy Research Abstracts
Author:
Publisher:
ISBN:
Category : Power resources
Languages : en
Pages : 922
Book Description
Semiannual, with semiannual and annual indexes. References to all scientific and technical literature coming from DOE, its laboratories, energy centers, and contractors. Includes all works deriving from DOE, other related government-sponsored information, and foreign nonnuclear information. Arranged under 39 categories, e.g., Biomedical sciences, basic studies; Biomedical sciences, applied studies; Health and safety; and Fusion energy. Entry gives bibliographical information and abstract. Corporate, author, subject, report number indexes.
Publisher:
ISBN:
Category : Power resources
Languages : en
Pages : 922
Book Description
Semiannual, with semiannual and annual indexes. References to all scientific and technical literature coming from DOE, its laboratories, energy centers, and contractors. Includes all works deriving from DOE, other related government-sponsored information, and foreign nonnuclear information. Arranged under 39 categories, e.g., Biomedical sciences, basic studies; Biomedical sciences, applied studies; Health and safety; and Fusion energy. Entry gives bibliographical information and abstract. Corporate, author, subject, report number indexes.
Scientific and Technical Aerospace Reports
Author:
Publisher:
ISBN:
Category : Aeronautics
Languages : en
Pages : 782
Book Description
Lists citations with abstracts for aerospace related reports obtained from world wide sources and announces documents that have recently been entered into the NASA Scientific and Technical Information Database.
Publisher:
ISBN:
Category : Aeronautics
Languages : en
Pages : 782
Book Description
Lists citations with abstracts for aerospace related reports obtained from world wide sources and announces documents that have recently been entered into the NASA Scientific and Technical Information Database.
Corrosion of Zircaloy-4 Tubing in 68OF Water (LWBR Development Program).
Author:
Publisher:
ISBN:
Category :
Languages : en
Pages :
Book Description
Seamless Zircaloy-4 tubing is utilized as fuel rod cladding in light water reactors. Water corrosion tests at 68OF have been performed to determine the corrosion and hydriding characteristics of Zircaloy-4 tubing, fabricated by cold reduction and finished in two metallurgical conditions: a stress-relief anneal (SRA) and a recrystallization anneal (RXA). These corrosion tests revealed differences in the post-transition corrosion product weight gains of the two materials. A computer corrosion model, designated CHORT, was developed from the test data and ascribes the observed difference in material weight gain to an assumed difference in the periodicity of a postulated cyclic buckling of the oxide.
Publisher:
ISBN:
Category :
Languages : en
Pages :
Book Description
Seamless Zircaloy-4 tubing is utilized as fuel rod cladding in light water reactors. Water corrosion tests at 68OF have been performed to determine the corrosion and hydriding characteristics of Zircaloy-4 tubing, fabricated by cold reduction and finished in two metallurgical conditions: a stress-relief anneal (SRA) and a recrystallization anneal (RXA). These corrosion tests revealed differences in the post-transition corrosion product weight gains of the two materials. A computer corrosion model, designated CHORT, was developed from the test data and ascribes the observed difference in material weight gain to an assumed difference in the periodicity of a postulated cyclic buckling of the oxide.
Corrosion Abstracts
Author:
Publisher:
ISBN:
Category : Corrosion and anti-corrosives
Languages : en
Pages : 652
Book Description
Publisher:
ISBN:
Category : Corrosion and anti-corrosives
Languages : en
Pages : 652
Book Description
CORROSION OF ZIRCALOY-4 TUBING IN 680F WATER. (LWBR DEVELOPMENT PROGRAM).
Nuclear Science Abstracts
INIS Atomindex
Government Reports Annual Index
Author:
Publisher:
ISBN:
Category : Government reports announcements & index
Languages : en
Pages : 1064
Book Description
Publisher:
ISBN:
Category : Government reports announcements & index
Languages : en
Pages : 1064
Book Description