Surface Fatigue Lives of Case-Carburized Gears With an Improved Surface Finish PDF Download
Are you looking for read ebook online? Search for your book and save it on your Kindle device, PC, phones or tablets. Download Surface Fatigue Lives of Case-Carburized Gears With an Improved Surface Finish PDF full book. Access full book title Surface Fatigue Lives of Case-Carburized Gears With an Improved Surface Finish by . Download full books in PDF and EPUB format.
Author: Publisher: ISBN: Category : Languages : en Pages : 18
Book Description
Previous research provides qualitative evidence that an improved surface finish can increase the surface fatigue lives of gears. To quantify the influence of surface roughness on life, a set of AISI 9310 steel gears was provided with a near-mirror finish by superfinishing. The effects of the superfinishing on the quality of the gear tooth surfaces were determined using data from metrology, profilometry, and interferometric microscope inspections. The superfinishing reduced the roughness average by about a factor of 5. The superfinished gears were subjected to surface fatigue testing at 1.71-GPa (248-ksi) Hertz contact stress, and the data were compared with the NASA Glenn gear fatigue data base. The lives of gears with superfinished teeth were about four times greater compared with the lives of gears with ground teeth but with otherwise similar quality.
Author: Publisher: ISBN: Category : Languages : en Pages : 18
Book Description
Previous research provides qualitative evidence that an improved surface finish can increase the surface fatigue lives of gears. To quantify the influence of surface roughness on life, a set of AISI 9310 steel gears was provided with a near-mirror finish by superfinishing. The effects of the superfinishing on the quality of the gear tooth surfaces were determined using data from metrology, profilometry, and interferometric microscope inspections. The superfinishing reduced the roughness average by about a factor of 5. The superfinished gears were subjected to surface fatigue testing at 1.71-GPa (248-ksi) Hertz contact stress, and the data were compared with the NASA Glenn gear fatigue data base. The lives of gears with superfinished teeth were about four times greater compared with the lives of gears with ground teeth but with otherwise similar quality.
Author: David G. Lewicki Publisher: ISBN: Category : Fracture mechanics Languages : en Pages : 186
Book Description
Analytical and experimental studies were performed to investigate the effect of rim thickness on gear tooth crack propagation. The goal was to determine whether cracks grew through gear teeth (benign failure mode) or through gear rims (catastrophic failure mode) for various rim thicknesses. The computer program used had an automated crack propagation option in which cracks were grown numerically using an automated re-meshing scheme. In addition, experimental studies were performed in the NASA Lewis Spur Gear Fatigue Rig. Good correlation between the predicted number of crack propagation cycles and measured number of cycles was achieved using both the Paris fatigue crack growth method and the Collipfiest crack growth equation when fatigue crack closure was considered.
Author: Advisory Committee on Technology and Society Publisher: National Academies Press ISBN: 9780309037860 Category : Social Science Languages : en Pages : 1298
Book Description
Cities and Their Vital Systems asks basic questions about the longevity, utility, and nature of urban infrastructures; analyzes how they grow, interact, and change; and asks how, when, and at what cost they should be replaced. Among the topics discussed are problems arising from increasing air travel and airport congestion; the adequacy of water supplies and waste treatment; the impact of new technologies on construction; urban real estate values; and the field of "telematics," the combination of computers and telecommunications that makes money machines and national newspapers possible.
Author: 
Author: 
Author: 
Author: 
Author: 
Author: 
Author: 
Author: David G. Lewicki
Author: 
Author: Advisory Committee on Technology and Society
Author: