Irradiation growth of zircaloy-2 in atr at 330 k : results obtained to 1996 March
Irradiation growth of zircaloy-2 at 330 k : results of measurements obtained to 1991 March in the atr reactor at idaho falls u.s.a
Irradiation growth of zircaloy-2 at 330k : results of measurements obtained to date in the atr reactor at idaho falls
Irradiation growth of zircaloy-2 in atr at 330 k : update of results obtained to 1991 March to include measured fluences
Irradiation growth of zircaloy-2 at 330 k : results of measurements obtained to 1988 September in the atr reactor at idaho falls
Irradiation growth of zircaloy-2 at 330k : results of measurements obtained to 1987 June in the atr reactor at idaho falls
Irradiation growth of zircaloy-2 at 330 k : results of measurements obtained to 1989 July in the atr reactor at idaho falls u.s.a
Irradiation growth of zircaloy-2 at 330 k : results of measurements after the second and third irradiation in the atr reactor at idaho falls
Author: M. A. Miller
Publisher:
ISBN:
Category :
Languages : en
Pages : 0
Book Description
This report summarizes the irradiation growth measurements on zircaloy-2 specimens after second and third irradiations in the advanced test reactor at idaho falls as part of a candev work package to investigate the dimensional stability of calandria tube materials. some specimens have reached fluences of 1 x 10 sup(26) n.m sup(-2), e greater than 1 mev, corresponding to the fluence of pickering calandria tubes after 30 years of operation. the results exhibit large variability in growth behaviour between calandria tube materials from different reactors. most specimens have not yet attained steady state growth rates even at higher fluences.
Publisher:
ISBN:
Category :
Languages : en
Pages : 0
Book Description
This report summarizes the irradiation growth measurements on zircaloy-2 specimens after second and third irradiations in the advanced test reactor at idaho falls as part of a candev work package to investigate the dimensional stability of calandria tube materials. some specimens have reached fluences of 1 x 10 sup(26) n.m sup(-2), e greater than 1 mev, corresponding to the fluence of pickering calandria tubes after 30 years of operation. the results exhibit large variability in growth behaviour between calandria tube materials from different reactors. most specimens have not yet attained steady state growth rates even at higher fluences.