Author: Michihiro TanakaPublisher:
ISBN:
Category :
Languages : en
Pages : 26
Book Description
Fatigue Crack Propagation in Welded Structural Steel Plates
Author: Michihiro TanakaFatigue of Welded Structures
Author: Timothy Russell GurneyPublisher: CUP Archive
ISBN: 9780521225588
Category : Technology & Engineering
Languages : en
Pages : 480
Book Description
Fatigue Strength of Welded Structures
Author: S J MaddoxPublisher: Woodhead Publishing
ISBN: 1845698797
Category : Technology & Engineering
Languages : en
Pages : 211
Book Description
The key to avoidance of fatigue, which is the main cause of service failures, is good design. In the case of welded joints, which are particularly susceptible to fatigue, design rules are available. However, their effective use requires a good understanding of fatigue and an appreciation of problems concerned with their practical application. Fatigue strength of welded structures has incorporates up-to-date design rules with high academic standards whilst still achieving a practical approach to the subject. The book presents design recommendations which are based largely on those contained in recent British standards and explains how they are applied in practice. Attention is also focused on the relevant aspects of fatigue in welded joints which are not yet incorporated in codes thus providing a comprehensive aid for engineers concerned with the design or assessment of welded components or structures. Background information is given on the fatigue lives of welded joints which will enable the engineer or student to appreciate why there is such a contrast between welded and unwelded parts, why some welded joints perform better than others and how joints can be selected to optimise fatigue performance.
Fatigue Crack Propagation Data Obtained from Parent Plate, Weld Metal and HAZ in Structural Steels
Author: S. J. MaddoxFatigue and Fracture
Author: F. C. CampbellPublisher: ASM International
ISBN: 1615039767
Category : Technology & Engineering
Languages : en
Pages : 699
Book Description
"This book emphasizes the physical and practical aspects of fatigue and fracture. It covers mechanical properties of materials, differences between ductile and brittle fractures, fracture mechanics, the basics of fatigue, structural joints, high temperature failures, wear, environmentally-induced failures, and steps in the failure analysis process."--publishers website.
Fatigue Crack Propagation in Welded Steel Plate
Author: Wee Liam ChongPublisher:
ISBN:
Category : Welded joints
Languages : en
Pages :
Book Description
Effect of Lack of Penetration on Fatigue Resistance of High-strength Structural Steel Welds
Author: Y. TobePublisher:
ISBN:
Category : Steel, Structural
Languages : en
Pages : 38
Book Description
Zero-to-tension fatigue tests were carried out on double-V butt welds of ASTM A514 steel plate, 20 mm in thickness, which contained full-length lack of penetration (LOP) defects. The fatigue crack initiation and propagation portions of the specimens' fatigue lives were experimentally separated. Compression-to-tension fatigue tests were carried out on prime base plate, as-welded sound joints, and reinforcement-removed welds to experimentally determine the fatigue strength reduction factor (Kf) of the LOP defects. LOP defects as small as 0.5 mm wide had a profound effect on fatigue life. The fatigue crack initiation life was found to be short-only 10 percent of the total life-and could be predicted using fatigue crack initiation concepts. The use of KF(max), the maximum possible fatigue strength reduction factor, was found to be appropriate. In a separate substudy, the fatigue resistance of ASTM A514 butt-welded joints containing clustered porosity was determined. (Author).
Early Fatigue Crack Growth at Welds
Author: C. C. MonahanPublisher: Computational Mechanics
ISBN:
Category : Technology & Engineering
Languages : en
Pages : 216
Book Description
Fatigue Crack Propagation in Notched Mild Steel Plates
Author: Fatigue and Fracture Testing of Weldments
Author: Harry I. McHenryPublisher: ASTM International
ISBN: 0803112777
Category : Welded joints
Languages : en
Pages : 310
Book Description
Fifteen papers from a symposium held in Sparks, Nev., April 1988. They cover: low and high cycle fatigue, fatigue crack growth, corrosion fatigue, fracture toughness testing, and wide-plate testing. Annotation copyright Book News, Inc. Portland, Or.