Author: L. Rouillon
Publisher:
ISBN:
Category : Deformation
Languages : en
Pages : 22
Book Description
The impact of irradiation damage accumulated in fuel claddings on their mechanical behavior and their susceptibility to iodine-induced stress corrosion cracking (I-SCC) was studied in irradiated zirconium and standard Zircaloy-4 sheets subjected to interrupted tension tests in methanol/iodine solutions and in an inert environment. The study of the I-SCC cracks has been carried out by SEM, while the characterization of the irradiation defects and the activated slip systems used TEM.