Author: Pascal FourvelPublisher:
ISBN:
Category :
Languages : fr
Pages :
Book Description
L'APPLICATION DIRECTE DE LA MECANIQUE LINEAIRE ELASTIQUE DE LA RUPTURE AUX CERAMIQUES ENDOMMAGEABLES POSE DE NOMBREUX PROBLEMES TOUCHANT AUX CONCEPTS DE BASE. D'AUTRE PART LES THEORIES ANALYTIQUES PORTANT SUR LA MODELISATION DU COMPORTEMENT DE COMPOSITES UNIDIRECTIONNELS NE PEUVENT PAS ETRE UTILISEES DANS LE CAS DE MATERIAUX COMPLEXES TELS LES MATERIAUX COMPOSITES A FIBRES TISSEES. CE TRAVAIL PORTE SUR L'ETUDE DU COMPORTEMENT THERMOMECANIQUE DE COMPOSITES A FIBRES TISSEES 2D. L'EXPERIENCE ACQUISE AU LABORATOIRE DANS L'ETUDE DU C-SIC NOUS A PERMIS DANS UN PREMIER TEMPS D'UTILISER DANS LE CAS DU SIC-SIC A TEMPERATURE AMBIANTE LES MODELES ENERGETIQUES PROPOSES DANS LA LITTERATURE, TENANT COMPTE DES PHENOMENES ANELASTIQUES. DANS UN SECOND TEMPS, NOUS AVONS COMPARE LE COMPORTEMENT DU SIC-SIC A L'AMBIANTE ET A HAUTE TEMPERATURE SOUS AIR. NOUS AVONS MONTRE QUE LE SIC-SIC DOIT SA HAUTE TENUE MECANIQUE AUX PROPRIETES DE L'INTERFACE QUI LAISSE GLISSER LA FIBRE DANS SA GAINE DE MATRICE, PERMETTANT DES LONGUEURS D'EXTRACTION DE FIBRES IMPORTANTES. C'EST EGALEMENT LA MODIFICATION DE CETTE INTERFACE QUI EST PRINCIPALEMENT RESPONSABLE DE LA DEGRADATION DES PROPRIETES MECANIQUES A HAUTE TEMPERATURE SOUS AIR. BIEN ENTENDU CES MATERIAUX NE SONT PAS UTILISABLES DANS CES CONDITIONS, A MOINS D'UTILISER UNE COUCHE PROTECTRICE