Author: OLIVIER.. QUESADA
Publisher:
ISBN:
Category :
Languages : fr
Pages : 159
Book Description
L'ACTION CONJUGUEE DE PARTICULES SOLIDES ANGULEUSES EN SUSPENSION DANS UN FLUIDE CORROSIF CONSTITUE UNE FORME DE DEGRADATION DES MATERIAUX APPELEE ABRASION-CORROSION. SA COMPLEXITE RESIDE DANS L'INTERACTION POSSIBLE DES DEUX TYPES D'ENDOMMAGEMENT (MECANIQUE ET ELECTROCHIMIQUE) CONDUISANT A UNE SYNERGIE, C'EST-A-DIRE A L'ACCENTUATION DE L'UN SOUS L'EFFET DE L'AUTRE. LA COMPLEXITE EST D'AUTANT PLUS GRANDE QUE L'ETUDE EST REALISEE SUR DES MATERIAUX PASSIVABLES ET QU'IL EXISTE DE CE FAIT UNE COMPETITION ENTRE LES CINETIQUES DE DEPASSIVATION ET DE REPASSIVATION DE L'ALLIAGE. L'OBJECTIF DE L'ETUDE ETAIT D'ETABLIR UN GUIDE DE CHOIX DE MATERIAUX PERMETTANT DE FACILITER LA SELECTION D'ACIERS INOXYDABLES EN SITUATION D'ABRASION-CORROSION. UNE ETUDE PARAMETRIQUE DU COMPORTEMENT D'ACIERS INOXYDABLES SOUMIS A L'ABRASION-CORROSION EN CONDITIONS REPRESENTATIVES DE MILIEUX INDUSTRIELS A ETE REALISEE. LES RESULTATS DES ESSAIS EN MILIEU NEUTRE OU LEGEREMENT CORROSIF (PH=8 OU 3) ONT MIS EN EVIDENCE LA PREPONDERANCE DE L'ENDOMMAGEMENT DE MATURE MECANIQUE. CELUI-CI S'ELEVE A ENVIRON 90% DE L'ENDOMMAGEMENT TOTAL ET SE MANIFESTE PAR UN ARRACHEMENT DE COPEAUX MICRONIQUES A LA SURFACE DE L'ACIER. LA DURETE INITIALE DES ACIERS APPARAIT ALORS COMME UN CRITERE DE CHOIX SATISFAISANT DU MATERIAU. EN REVANCHE, UNE DUCTILITE ELEVEE (A% > 40) S'AVERE DEFAVORABLE. EN TERMES DE PERFORMANCE, LES ACIERS SE CLASSENT AINSI : AUSTENITIQUES