Author: M. H. MuellerPublisher:
ISBN:
Category : Nuclear fuel rods
Languages : en
Pages : 36
Book Description
Effect of Varying Reduction on the Preferred Orientation in Rolled Uranium Rods
Author: M. H. MuellerPublisher:
ISBN:
Category : Nuclear fuel rods
Languages : en
Pages : 36
Book Description
Effect of Rolling Temperature on the Preferred Orientation in Rolled Uranium Rods
Author: M. H. MuellerPublisher:
ISBN:
Category : Metallurgy
Languages : en
Pages : 38
Book Description
A study has been made of the radial symmetry of the texture produced by two different types of roll passes. A plot of the radial distribution of the (002) poles indicated an asymmetric pattern with the oval, edge-oval pass sequence and a rather uniform distribution of these poles with the hand round roll passes.
EFFECT OF ROLLING TEMPERATURE ON THE PREFERRED ORIENTATION IN ROLLED URANIUM RODS. Final Report-Metallurgy Program 4.1.9
Author: Preferred Orientation in Cross-rolled Uranium
Author: G. R. MallettPublisher:
ISBN:
Category : Rolling (Metal-work)
Languages : en
Pages : 50
Book Description
A study is made of the preferred orientation that occurs as a result of cross-rolling uranium sheet. The study is made by the use of inverse-pole figures and calculated thermal expansion coefficients.
Papers Presented at the X-ray Preferred Orientation Meeting at Savannah River Laboratory, June 7, 8, 1962
Author: Edward F. SturckenPublisher:
ISBN:
Category : Uranium enrichment
Languages : en
Pages : 134
Book Description
Papers Presented at the X-ray Preferred Orientation Meeting Held at National Lead Company of Ohio, November 9 and 10, 1959
Author: Edward F. SturckenPublisher:
ISBN:
Category : Uranium enrichment
Languages : en
Pages : 68
Book Description
PREFERRED ORIENTATION IN ROLLED AND IN RECRYSTALLIZED HIGH-PURITY URANIUM ROD. Final Report of Metallurgy Program.4.1.17
Author: Publisher:
ISBN:
Category :
Languages : en
Pages :
Book Description
The preferred orientation of a relatively small piece of high-purity uranium rod, rolled to an 85% reduction at 300 deg C, has been determined in the as-rolled and in the recrystallized conditions. The 12 different charts obtained indicated that the as-rolled texture could be described as a duplex (041) and (352) with the (041) being the major component and with considerable spread about each component. The recrystallized rod showed approximate (041) and (392) components with considerable spread. These texture components for both the as- rolled and the recrystallized rods are not too different from those previously reported for reactor-grade uranium rod. However, it was noted that the texture appeared to be quite sharp for the reduction used, and the maximum intensity on an inverse pole figure was considerably displaced from the periphery of an (001) standard projection for both the rolled and recrystallized rods. (auth).
Preferred Orientation of Cold-rolled and Recrystallized Uranium Plate
Author: William R. McDonellPublisher:
ISBN:
Category : Recrystallization (Metallurgy)
Languages : en
Pages : 24
Book Description
Effects of Rolling and Heat Treatment on Anisotropic Irradiation Growth of Uranium
Author: J. H. KittelPublisher:
ISBN:
Category : Irradiation
Languages : en
Pages : 38
Book Description
An investigation was made to determine the effect of rolling temperature, roll pass design, amount of reduction, and heat treatment before and after rolling on the anisotropic growth rate of uranium under irradiation. The growth rate was found to increase with decreasing rolling temperature and with increasing reduction of area at 300 deg C. The rate of elongation was proportional to the amount of (010) component present or, where shortening occurred, to the amount of (100) component. Oval-edge-oval roll passes resulted in somewhat higher irradiation growth rates than did round roll passes. Recrystallization after rolling effectively reduced the irradiation growth rate of uranium rolled at temperatures of 500 deg C and lower. Irradiation caused length shortening in uranium which was beta quenched after being round-rolled at temperatures of 400 deg C and above, and which was beta quenched after being oval- rolled at temperatures of 300 deg C and above.
Preferred Orientation in Rolled and in Recystallized High-purity Uranium Rod
Author: M. H. MuellerPublisher:
ISBN:
Category : Anisotropy
Languages : en
Pages : 32
Book Description
The preferred orientation of a relatively small piece of high-purity uranium rod, rolled to an 85% reduction at 300 deg C, has been determined in the as-rolled and in the recrystallized conditions. The 12 different charts obtained indicated that the as-rolled texture could be described as a duplex (041) and (352) with the (041) being the major component and with considerable spread about each component. The recrystallized rod showed approximate (041) and (392) components with considerable spread. These texture components for both the as- rolled and the recrystallized rods are not too different from those previously reported for reactor-grade uranium rod. However, it was noted that the texture appeared to be quite sharp for the reduction used, and the maximum intensity on an inverse pole figure was considerably displaced from the periphery of an (001) standard projection for both the rolled and recrystallized rods.